| 规格级别 | 刚性，良好,辛烯共聚单体,良好的热封性,韧性良好,可加工性，良好,良好的强度,食品接触的合规性,中等密度,抗结块性 薄膜挤出 | 外观颜色 | |
| 该料用途 | 工业应用,薄膜,包装,建筑应用领域,衬里,袋子 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 0.926 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 0.80 | g/10min | |
| 薄膜 | 薄膜厚度-经测试 | 2576 | µm | ||
| 薄膜 | SecantModulus-1%Secant,MD | 25µm,吹塑薄膜 | ASTMD882 | 234 | MPa |
| 薄膜 | SecantModulus-1%Secant,MD | 76µm,BlownFilm | ASTMD882 | 230 | MPa |
| 薄膜 | SecantModulus-1%Secant,TD | 25µm,吹塑薄膜 | ASTMD882 | 251 | MPa |
| 薄膜 | SecantModulus-1%Secant,TD | 76µm,BlownFilm | ASTMD882 | 260 | MPa |
| 薄膜 | 抗张强度-MD | Yield,25µm,BlownFilm | ASTMD882 | 11.0 | MPa |
| 薄膜 | 抗张强度-MD | Yield,76µm,BlownFilm | ASTMD882 | 12.0 | MPa |
| 薄膜 | TensileStrength-TD | Yield,25µm,BlownFilm | ASTMD882 | 12.0 | MPa |
| 薄膜 | TensileStrength-TD | Yield,76µm,BlownFilm | ASTMD882 | 12.0 | MPa |
| 薄膜 | 伸长率-MD | Break,25µm,BlownFilm | ASTMD882 | 490 | % |
| 薄膜 | 伸长率-MD | Break,76µm,BlownFilm | ASTMD882 | 630 | % |
| 薄膜 | TensileElongation-TD | Break,25µm,BlownFilm | ASTMD882 | 710 | % |
| 薄膜 | TensileElongation-TD | Break,76µm,BlownFilm | ASTMD882 | 680 | % |
| 薄膜 | 落锤冲击 | 25µm,吹塑薄膜 | ASTMD1709A | 160 | g |
| 薄膜 | 落锤冲击 | 76µm,BlownFilm | ASTMD1709A | 450 | g |
| 薄膜 | 埃尔曼多夫抗撕强度-MD | 25µm,吹塑薄膜 | ASTMD1922 | 300 | g |
| 薄膜 | 埃尔曼多夫抗撕强度-MD | 76µm,BlownFilm | ASTMD1922 | 1100 | g |
| 薄膜 | ElmendorfTearStrength-TD | 25µm,吹塑薄膜 | ASTMD1922 | 750 | g |
| 薄膜 | ElmendorfTearStrength-TD | 76µm,BlownFilm | ASTMD1922 | 1500 | g |
| 光学性能 | 光泽度 | 45°,25.4µm,BlownFilm | ASTMD2457 | 50 | |
| 光学性能 | 光泽度 | 45°,76.2µm,BlownFilm | ASTMD2457 | 61 | |
| 光学性能 | 雾度 | 25.4µm,吹塑薄膜 | ASTMD1003 | 14 | % |
| 光学性能 | 雾度 | 76.2µm,BlownFilm | ASTMD1003 | 17 | % |
| ADDITIONAL INFORMATION | 补充信息 | TestMethod | NominalValue | Unit | |
| ADDITIONAL INFORMATION | LowFrictionPuncture-BlownFilm | 25.4µm | InternalMethod | 250 | J/cm |
| ADDITIONAL INFORMATION | LowFrictionPuncture-BlownFilm | 76.2µm | InternalMethod | 200 | J/cm |