| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.919 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 2.1 | g/10min | |
| 薄膜 | 薄膜厚度-经测试 | ASTMD746 | 30 | µm | |
| 薄膜 | 抗张强度 | MD:屈服,30µm | ASTMD882 | 10.8 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,30µm | ASTMD882 | 10.8 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,30µm | ASTMD882 | 39.2 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,30µm | ASTMD882 | 35.3 | MPa |
| 薄膜 | 伸长率 | MD:断裂,30µm | ASTMD882 | 700 | % |
| 薄膜 | 伸长率 | TD:断裂,30µm | ASTMD882 | 750 | % |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:30µm | ASTMD1922 | 300 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:30µm | ASTMD1922 | 360 | g |
| 薄膜 | SpencerImpact(30.0µm) | ASTMD3420 | 0.588 | J | |
| 薄膜 | 薄膜厚度-经测试 | ASTMD746 | 30 | µm | |
| 薄膜 | 抗张强度 | MD:屈服,30µm | ASTMD882 | 10.8 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,30µm | ASTMD882 | 10.8 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,30µm | ASTMD882 | 39.2 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,30µm | ASTMD882 | 35.3 | MPa |
| 薄膜 | 伸长率 | MD:断裂,30µm | ASTMD882 | 700 | % |
| 薄膜 | 伸长率 | TD:断裂,30µm | ASTMD882 | 750 | % |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:30µm | ASTMD1922 | 300 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:30µm | ASTMD1922 | 360 | g |
| 薄膜 | SpencerImpact(30.0µm) | ASTMD3420 | 0.588 | J | |
| 热性能 | 脆化温度 | ASTMD746 | <-70.0 | °C | |
| 热性能 | 维卡软化温度 | ASTMD1525 | 102 | °C | |
| 光学性能 | 雾度 | ASTMD1003 | 2.0 | % | |