| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.916 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.65 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
25 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD(25µm,BlownFilm) |
|
ASTMD882 |
126 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(25µm,BlownFilm) |
|
ASTMD882 |
138 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,25µm,BlownFilm) |
|
ASTMD882 |
8.50 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,25µm,BlownFilm) |
|
ASTMD882 |
8.50 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,25µm,BlownFilm) |
|
ASTMD882 |
47.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,25µm,BlownFilm) |
|
ASTMD882 |
44.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,25µm,BlownFilm) |
|
ASTMD882 |
470 |
% |
| 薄膜 |
TensileElongation-TD(Break,25µm,BlownFilm) |
|
ASTMD882 |
780 |
% |
| 薄膜 |
落锤冲击(25µm,吹塑薄膜) |
|
ASTMD1709A |
700 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(25µm,BlownFilm) |
|
ASTMD1922 |
350 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(25µm,BlownFilm) |
|
ASTMD1922 |
430 |
g |
| 薄膜 |
SealInitiationTemperature2(25µm,BlownFilm) |
|
|
100 |
°C |
| 光学性能 |
光泽度 |
45°,25.0µm,BlownFilm3 |
ASTMD2457 |
72 |
|
| 光学性能 |
光泽度 |
45°,25.0µm,BlownFilm4 |
ASTMD2457 |
38 |
|
| 光学性能 |
雾度 |
25.0µm,BlownFilm3 |
ASTMD1003 |
7.0 |
% |
| 光学性能 |
雾度 |
25.0µm,BlownFilm4 |
ASTMD1003 |
15 |
% |
| ADDITIONAL INFORMATION |
补充信息 |
|
TestMethod |
NominalValue |
Unit |
| ADDITIONAL INFORMATION |
LowFrictionPuncture-BlownFilm(25.0µm) |
|
|
980 |
J/cm |