| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.918 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
1.0 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
25 |
µm |
| 薄膜 |
割线模量-1%正割,MD(25µm) |
|
ASTMD882 |
200 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(25µm) |
|
ASTMD882 |
224 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,25µm) |
|
ASTMD882 |
55.8 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,25µm) |
|
ASTMD882 |
42.1 |
MPa |
| 薄膜 |
伸长率-MD(断裂,25µm) |
|
ASTMD882 |
580 |
% |
| 薄膜 |
TensileElongation-TD(Break,25µm) |
|
ASTMD882 |
700 |
% |
| 薄膜 |
落锤冲击(25µm,吹塑薄膜) |
|
ASTMD1709A |
190 |
g |
| 薄膜 |
总能量冲击(25µm,吹塑薄膜) |
|
ASTMD4272 |
2.44 |
J |
| 薄膜 |
埃尔曼多夫抗撕强度-MD(25µm) |
|
ASTMD1922 |
330 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(25µm) |
|
ASTMD1922 |
650 |
g |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
105 |
°C |
| 光学性能 |
光泽度(45°,25.4µm,吹塑薄膜) |
|
ASTMD2457 |
35 |
|
| 光学性能 |
雾度(25.4µm,吹塑薄膜) |
|
ASTMD1003 |
22 |
% |