| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.925 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
3.5 |
g/10min |
| 薄膜 |
SecantModulus-1%Secant,MD |
13µm |
ASTMD882 |
252 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,MD |
38µm |
ASTMD882 |
307 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD |
13µm |
ASTMD882 |
255 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD |
38µm |
ASTMD882 |
314 |
MPa |
| 薄膜 |
抗张强度-MD |
Break,13µm |
ASTMD882 |
9.65 |
MPa |
| 薄膜 |
抗张强度-MD |
Break,38µm |
ASTMD882 |
33.1 |
MPa |
| 薄膜 |
TensileStrength-TD |
Break,13µm |
ASTMD882 |
7.24 |
MPa |
| 薄膜 |
TensileStrength-TD |
Break,38µm |
ASTMD882 |
23.4 |
MPa |
| 薄膜 |
伸长率-MD |
Break,13µm |
ASTMD882 |
500 |
% |
| 薄膜 |
伸长率-MD |
Break,38µm |
ASTMD882 |
690 |
% |
| 薄膜 |
TensileElongation-TD |
Break,13µm |
ASTMD882 |
630 |
% |
| 薄膜 |
TensileElongation-TD |
Break,38µm |
ASTMD882 |
740 |
% |
| 薄膜 |
落锤冲击 |
13µm,BlownFilm |
ASTMD1709 |
30 |
g |
| 薄膜 |
落锤冲击 |
38µm,BlownFilm |
ASTMD1709 |
110 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD |
13µm |
ASTMD1922 |
40 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD |
38µm |
ASTMD1922 |
100 |
g |
| 薄膜 |
ElmendorfTearStrength-TD |
13µm |
ASTMD1922 |
180 |
g |
| 薄膜 |
ElmendorfTearStrength-TD |
38µm |
ASTMD1922 |
220 |
g |
| 光学性能 |
光泽度 |
45°,12.7µm,BlownFilm |
ASTMD2457 |
60 |
|
| 光学性能 |
光泽度 |
45°,38.1µm,BlownFilm |
ASTMD2457 |
25 |
|
| 光学性能 |
雾度 |
12.7µm,BlownFilm |
ASTMD1003 |
25 |
% |
| 光学性能 |
雾度 |
38.1µm,BlownFilm |
ASTMD1003 |
30 |
% |