| 规格级别 | 其它 薄膜 吹塑,挤出 | 外观颜色 | |
| 该料用途 | 薄膜 拉伸缠绕 | ||
| 备注说明 | 共聚物 己烯共聚单体 抗撞击性，良好 良好的撕裂强度 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 0.917 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 0.90 |
g/10 min
|
|
|
割线模量
|
1% 正割, MD
|
ASTM D882 | 165 |
MPa
|
|
|
1% 正割, TD
|
ASTM D882 | 186 |
MPa
|
||
| 机械性能 |
抗张强度
|
MD : 屈服
|
ASTM D882 | 8.96 |
MPa
|
|
TD : 屈服
|
ASTM D882 | 9.65 |
MPa
|
||
|
MD : 断裂
|
ASTM D882 | 62.7 |
MPa
|
||
|
TD : 断裂
|
ASTM D882 | 51.0 |
MPa
|
||
|
伸长率
|
MD : 断裂
|
ASTM D882 | 630 | % | |
|
TD : 断裂
|
ASTM D882 | 720 | % | ||
|
落锤冲击
|
ASTM D1709A | 330 |
g
|
||
|
埃尔曼多夫抗撕强度
|
MD
|
ASTM D1922 | 460 | g | |
| TD | ASTM D1922 | 600 | g | ||
| 光学性能 | 光泽度 | 45° | ASTM D2457 | 37 | |
|
雾度
|
ASTM D1003 | 17 | % | ||