LLDPE | LL-1002
生产厂家：埃克森美孚
规格用途
| 规格级别 |
其它 薄膜 其它 |
外观颜色 |
|
| 该料用途 |
包装袋、伸展薄膜、罐子、箱衬垫 |
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
|
ASTM D-1238 |
2.0 |
g/10min |
| 密度 |
|
ExxonMobil Method |
0.918 |
g/cm3 |
| 机械性能 |
极限伸长率 |
MD |
|
ASTM D-882 |
700 |
% |
| TD |
|
ASTM D-882 |
830 |
% |
| Elmendorf断裂强度 |
MD |
|
ASTM D-1922 |
150 |
g |
| TD |
|
ASTM D-1922 |
340 |
g |
| 断裂拉伸强度 |
MD |
|
ASTM D-882 |
5800 |
psi(MPa) |
| TD |
|
ASTM D-882 |
4800 |
psi(MPa) |
| 热性能 |
熔点 |
|
ExxonMobil Method |
249(121) |
℉(℃) |
| 其它性能 |
击穿 |
|
ExxonMobil Method |
20 |
in.lb |
| 计量 |
|
ASTM D-374 |
1.2 |
mil |
| 1%割线模量 |
MD |
|
ASTM D-882 |
28 |
psi(MPa) |
| TD |
|
ASTM D-882 |
33 |
psi(MPa) |
| 混浊度 |
|
ASTM D-1003 |
18 |
% |
| 屈服拉伸强度 |
MD |
|
ASTM D-882 |
1400 |
psi(MPa) |
| TD |
|
ASTM D-882 |
1400 |
psi(MPa) |
| 光泽度 |
|
ASTM D-2457 |
40 |
|
-
-