| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.918 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/21.6kg) | ASTMD1238 | 3.0 | g/10min | |
| 机械性能 | 抗张强度(极限) | ASTMD638 | 15.0 | MPa | |
| 机械性能 | 伸长率(断裂) | ASTMD638 | 650 | % | |
| 薄膜 | 薄膜厚度-经测试 | 38 | µm | ||
| 薄膜 | 割线模量 | 1%正割,MD:38µm | ASTMD882 | 150 | MPa |
| 薄膜 | 割线模量 | 1%正割,TD:38µm | ASTMD882 | 154 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,38µm | ASTMD882 | 30.0 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,38µm | ASTMD882 | 25.0 | MPa |
| 薄膜 | 伸长率 | MD:断裂,38µm | ASTMD882 | 450 | % |
| 薄膜 | 伸长率 | TD:断裂,38µm | ASTMD882 | 650 | % |
| 薄膜 | 落锤冲击(38µm) | ASTMD1709A | 120 | g | |
| 薄膜 | 薄膜厚度-经测试 | 38 | µm | ||
| 薄膜 | 割线模量 | 1%正割,MD:38µm | ASTMD882 | 150 | MPa |
| 薄膜 | 割线模量 | 1%正割,TD:38µm | ASTMD882 | 154 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,38µm | ASTMD882 | 30.0 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,38µm | ASTMD882 | 25.0 | MPa |
| 薄膜 | 伸长率 | MD:断裂,38µm | ASTMD882 | 450 | % |
| 薄膜 | 伸长率 | TD:断裂,38µm | ASTMD882 | 650 | % |
| 薄膜 | 落锤冲击(38µm) | ASTMD1709A | 120 | g | |
| 热性能 | 脆化温度 | ASTMD746 | <-70.0 | °C | |
| 热性能 | 维卡软化温度 | ASTMD1525 | 94.0 | °C | |
| 光学性能 | 光泽度(45°,38.0µm) | ASTMD2457 | 90 | ||
| 光学性能 | 雾度(38.0µm) | ASTMD1003 | 4.0 | % | |