LLDPE | HS-7065 NT 7
生产厂家：美国陶氏
规格用途
| 规格级别 |
其它 薄膜 吹塑 |
外观颜色 |
|
| 该料用途 |
垃圾袋及重型包装袋 |
| 备注说明 |
良好的韧性和刚度 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTM D-792 |
0.9289 |
g/cm3 |
| 熔体流动速率 |
190℃/2.16 kg |
ASTM D-1238 |
0.8 |
g/10min |
| 厚度 |
|
|
20.3 |
microns |
| 粘连性 |
|
|
4000 |
ppm |
| 机械性能 |
拉伸屈服强度 |
MD |
ASTM D-882 |
16.6 |
MPa
|
| 拉伸屈服强度 |
TD |
ASTM D-882 |
19.6 |
MPa |
| 断裂伸长率 |
MD |
ASTM D-882 |
703 |
% |
| 断裂伸长率 |
TD |
ASTM D-882 |
793 |
% |
| 冲击强度 |
TD |
ASTM D-882 |
3701 |
|
| 冲击强度 |
MD |
ASTM D-882 |
4832 |
|
| 割线模量 |
MD，2% |
ASTM D-882 |
0.298577 |
GPa |
| 割线模量 |
TD，2% |
ASTM D-882 |
0.282975 |
GPa |
| 埃尔曼多夫撕裂强度 |
MD |
ASTM D-1922 |
171 |
g |
| 埃尔曼多夫撕裂强度 |
TD |
ASTM D-1922 |
715 |
g |
| 埃尔曼多夫撕裂强度 |
MD |
ASTM D-1922 |
8.42 |
g/micron |
| 埃尔曼多夫撕裂强度 |
TD |
ASTM D-1922 |
35.2 |
g/micron |
| 落锤冲击 |
Method B |
ASTM D-1709 |
Max100 |
g |
| 落锤冲击 |
Method A |
ASTM D-1709 |
55 |
g |
| 拉伸断裂强度 |
MD |
ASTM D-882 |
48.5 |
MPa |
| 拉伸断裂强度 |
TD |
ASTM D-882 |
54 |
MPa |
| 热封强度 |
|
Dow Method |
13.3 |
N |
| 热性能 |
热封强度始封温度 |
|
Dow Method |
120 |
℃ |
| 熔点 |
|
|
126 |
℃ |
| 维卡软化点 |
|
|
116 |
℃ |
| 光学性能 |
雾度 |
|
|
9 |
% |
| 光泽度 |
20 ° |
|
73 |
% |
| 光泽度 |
45 ° |
|
77 |
% |
-
-