| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 0.920 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 0.90 |
g/10 min
|
|
| 薄膜 | 薄膜厚度 |
经测试
|
25 |
µm
|
|
| 膜刺穿强度 | 25 µm | Internal Method | 4.97 |
J
|
|
| 膜刺穿力 |
25 µm
|
Internal Method | 53.4 |
N
|
|
| 膜耐刺穿性 |
25 µm
|
Internal Method | 25.2 |
J/cm³
|
|
|
膜强度
|
MD : 25 µm
|
ASTM D882 | 113 |
J/cm³
|
|
|
TD : 25 µm
|
ASTM D882 | 131 |
J/cm³
|
||
|
割线模量
|
1% 正割, MD : 25 µm
|
ASTM D882 | 235 |
MPa
|
|
|
2% 正割, MD : 25 µm
|
ASTM D882 | 207 |
MPa
|
||
|
2% 正割, MD : 51 µm
|
ASTM D882 | 173 |
MPa
|
||
|
1% 正割, TD : 25 µm
|
ASTM D882 | 265 |
MPa
|
||
|
2% 正割, TD : 25 µm
|
ASTM D882 | 225 |
MPa
|
||
|
2% 正割, TD : 51 µm
|
ASTM D882 | 181 |
MPa
|
||
|
抗张强度
|
MD : 屈服, 25 µm
|
ASTM D882 | 10.8 |
MPa
|
|
|
MD : 屈服, 51 µm
|
ASTM D882 | 11.0 |
MPa
|
||
|
TD : 屈服, 25 µm
|
ASTM D882 | 11.3 |
MPa
|
||
|
TD : 屈服, 51 µm
|
ASTM D882 | 10.9 |
MPa
|
||
|
MD : 断裂, 25 µm
|
ASTM D882 | 45.4 |
MPa
|
||
|
MD : 断裂, 51 µm
|
ASTM D882 | 37.7 |
MPa
|
||
|
TD : 断裂, 25 µm
|
ASTM D882 | 41.6 |
MPa
|
||
|
TD : 断裂, 51 µm
|
ASTM D882 | 41.9 |
MPa
|
||
|
伸长率
|
MD : 断裂, 25 µm
|
ASTM D882 | 570 | % | |
|
MD : 断裂, 51 µm
|
ASTM D882 | 580 | % | ||
|
TD : 断裂, 25 µm
|
ASTM D882 | 750 | % | ||
|
TD : 断裂, 51 µm
|
ASTM D882 | 720 | % | ||
| 落锤冲击 | 25 µm | ASTM D1709A | 210 |
g
|
|
|
51 µm
|
ASTM D1709A | 340 |
g
|
||
| 埃尔曼多夫抗撕强度 |
MD : 25 µm
|
ASTM D1922 | 360 |
g
|
|
|
MD : 51 µm
|
ASTM D1922 | 850 |
g
|
||
|
TD : 25 µm
|
ASTM D1922 | 640 |
g
|
||
|
TD : 51 µm
|
ASTM D1922 | 1100 |
g
|
||
| 热性能 |
维卡软化温度
|
ASTM D1525 | 107 | ℃ | |
| 溶融温度 | DSC | Internal Method | 119 | ℃ | |
| 光学性能 | 光泽度 |
45°, 25.4 µm
|
ASTM D2457 | 41 | |
|
45°, 50.8 µm
|
ASTM D2457 | 81 | |||
| 雾度 |
25.4 µm
|
ASTM D1003 | 16 | % | |
|
50.8 µm
|
ASTM D1003 | 8.8 | % | ||