| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
| 该料用途 | 重型包装袋，衬里，层压和高摩擦薄膜 | ||
| 备注说明 | 较高穿刺性，高摩擦系数（摩擦）和高焊缝破裂阻力，含有加工助剂和开口剂 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||
| 基本性能 | 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.73 | g/10min | ||||
| 密度 | ASTM D-1505 | 0.922 | g/cm3 | ||||||
| 机械性能 | 拉伸屈服强度 | ASTM D-882 |
|
MPa | |||||
| 拉伸断裂强度 | ASTM D-882 |
|
MPa | ||||||
| 屈服伸长率 | ASTM D-882 |
|
% | ||||||
| 断裂伸长率 | ASTM D-882 |
|
% | ||||||
| 埃尔曼多夫撕裂强度 | ASTM D-1922 |
|
Kgf/cm | ||||||
| 落镖冲击 | ASTM D-1709A | 140 | gf-50%F | ||||||
| 摩擦系数 | 动态 | ASTM D-1894 | 0.6 | ||||||
| 拉伸屈服强度 | ASTM D-638 | 13 | MPa | ||||||
| 拉伸断裂强度 | ASTM D-638 | 26 | MPa | ||||||
| 屈服伸长率 | ASTM D-638 | 16 | % | ||||||
| 断裂伸长率 | ASTM D-638 | 660 | % | ||||||
| 1%正割模量 | ASTM D-638 | 445 | MPa | ||||||
| 硬度 | ASTM D-2240 | 52 | |||||||
| 热性能 | 维卡软化温度 | ASTM D-1525 | 107 | ℃ | |||||
| 光学性能 | 雾度 | ASTM D-1003 | 14 | % | |||||
| 光泽度 | 45° | ASTM D-2457 | 50 | ||||||