| 规格级别 | 可加工性，良好,光学性能 薄膜挤出,吹塑薄膜 | 外观颜色 | |
| 该料用途 | 层压板,薄膜 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.920 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 1.6 | g/10min | |
| 机械性能 | 抗张强度(断裂) | ASTMD638 | 16.7 | MPa | |
| 机械性能 | 伸长率(断裂) | ASTMD638 | 800 | % | |
| 薄膜 | 薄膜厚度-经测试 | 30 | µm | ||
| 薄膜 | 抗张强度 | MD:断裂,30µm | ASTMD882 | 34.3 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,30µm | ASTMD882 | 30.4 | MPa |
| 薄膜 | 伸长率 | MD:断裂,30µm | ASTMD882 | 700 | % |
| 薄膜 | 伸长率 | TD:断裂,30µm | ASTMD882 | 800 | % |
| 薄膜 | 落锤冲击(30µm) | ASTMD1709 | 80 | g | |
| 薄膜 | TensileTearStrength | MD:30.0µm | ASTMD1004 | 137.3 | kN/m |
| 薄膜 | TensileTearStrength | TD:30.0µm | ASTMD1004 | 147.1 | kN/m |
| 薄膜 | 薄膜厚度-经测试 | 30 | µm | ||
| 薄膜 | 抗张强度 | MD:断裂,30µm | ASTMD882 | 34.3 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,30µm | ASTMD882 | 30.4 | MPa |
| 薄膜 | 伸长率 | MD:断裂,30µm | ASTMD882 | 700 | % |
| 薄膜 | 伸长率 | TD:断裂,30µm | ASTMD882 | 800 | % |
| 薄膜 | 落锤冲击(30µm) | ASTMD1709 | 80 | g | |
| 薄膜 | TensileTearStrength | MD:30.0µm | ASTMD1004 | 137.3 | kN/m |
| 薄膜 | TensileTearStrength | TD:30.0µm | ASTMD1004 | 147.1 | kN/m |
| 热性能 | 脆化温度 | ASTMD746 | <-76.0 | °C | |
| 热性能 | 维卡软化温度 | ASTMD1525 | 98.0 | °C | |
| 光学性能 | 雾度(30.0µm) | ASTMD1003 | 6.0 | % | |