LLDPE | FT860
生产厂家：韩国SK
规格用途
| 规格级别 |
其它 薄膜 其它 |
外观颜色 |
|
| 该料用途 |
制造伸直纸卷铸造薄膜而研制 |
| 备注说明 |
具有优秀的刚性延伸性、引张强度、无胶凝和加工性 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
|
ASTM D-1238 |
2.8 |
g/10min |
| 密度 |
|
ASTM D-1505 |
0.928 |
g/cm3 |
| 机械性能 |
撕裂强度 |
MD |
|
ASTM D-1004 |
8 |
Kg/cm |
| TD |
|
ASTM D-1004 |
10 |
Kg/cm |
| 伸长率 |
MD |
|
ASTM D-882 |
740 |
% |
| TD |
|
ASTM D-882 |
810 |
% |
| 拉伸屈服强度 |
MD |
|
ASTM D-882 |
140 |
Kg/cm2 |
| TD |
|
ASTM D-882 |
140 |
Kg/cm2 |
| 抗冲击强度 |
|
ASTM D-3420 |
5 |
Kg/cm |
| 拉伸断裂强度 |
MD |
|
ASTM D-882 |
460 |
Kg/cm2 |
| TD |
|
ASTM D-882 |
430 |
Kg/cm2 |
| 撕裂弹性率 |
MD |
|
ASTM D-882 |
2800 |
Kg/cm2 |
| TD |
|
ASTM D-882 |
3300 |
Kg/cm2 |
| 热性能 |
脆化温度 |
|
ASTM D-746 |
<-80 |
℃ |
| 维卡软化点 |
|
ASTM D-1525 |
105 |
℃ |
| 其它性能 |
雾度 |
|
ASTM D-1003 |
5 |
% |
| 薄膜厚度 |
|
ASTM D-746 |
30 |
µm |
-
-