| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.919 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
2.0 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
20 |
µm |
| 薄膜 |
TensileStrength-MD(Break,20µm,CastFilm) |
|
ASTMD882 |
44.8 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,20µm,CastFilm) |
|
ASTMD882 |
34.5 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,20µm,CastFilm) |
|
ASTMD882 |
500 |
% |
| 薄膜 |
TensileElongation-TD(Break,20µm,CastFilm) |
|
ASTMD882 |
920 |
% |
| 薄膜 |
落锤冲击(20µm,铸造薄膜) |
|
ASTMD1709 |
93 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(20µm,CastFilm) |
|
ASTMD1922 |
300 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(20µm,CastFilm) |
|
ASTMD1922 |
630 |
g |
| 光学性能 |
光泽度(45°,20.0µm,铸造薄膜) |
|
ASTMD523 |
98 |
|
| 光学性能 |
雾度(20.0µm,铸造薄膜) |
|
ASTMD1003 |
1.7 |
% |