| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.919 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.95 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
25 |
µm |
| 薄膜 |
TensileStrength-MD(Break,25µm,BlownFilm) |
|
ASTMD882 |
35.2 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,25µm,BlownFilm) |
|
ASTMD882 |
28.5 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,25µm,BlownFilm) |
|
ASTMD882 |
690 |
% |
| 薄膜 |
TensileElongation-TD(Break,25µm,BlownFilm) |
|
ASTMD882 |
920 |
% |
| 薄膜 |
埃尔曼多夫抗撕强度2 |
MD:25.0µm |
ASTMD1922 |
57.9 |
kN/m |
| 薄膜 |
埃尔曼多夫抗撕强度2 |
TD:25.0µm |
|
148.6 |
kN/m |
| 光学性能 |
Gardner光泽度(45°,25.0µm,吹塑薄膜) |
|
ASTMD523 |
40 |
|
| 光学性能 |
雾度(25.0µm,吹塑薄膜) |
|
ASTMD1003 |
20 |
% |
| ADDITIONAL INFORMATION |
补充信息 |
|
TestMethod |
NominalValue |
Unit |
| ADDITIONAL INFORMATION |
DartImpact2(25.0µm) |
|
ASTMD1709 |
52.1 |
kN/m |