| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
| 该料用途 | 制造吹制薄膜而研制出的中密度辛烷聚乙烯 | ||
| 备注说明 | 具有优秀的引裂强度、刚性、密封强度和加工性，还有良好的薄膜外观（低发裂） | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.928 | g/cm3 | ||
| 熔体流动速率 | ASTM D-1238 | 1 | g/10min | |||
| 机械性能 | 拉伸屈服强度 | MD | ASTM D-882 | 165 | Kg/cm2 | |
| TD | ASTM D-882 | 150 | Kg/cm2 | |||
| 拉伸断裂强度 | MD | ASTM D-882 | 590 | Kg/cm2 | ||
| TD | ASTM D-882 | 530 | Kg/cm2 | |||
| 伸长率 | MD | ASTM D-882 | 700 | % | ||
| TD | ASTM D-882 | 800 | % | |||
| 撕裂强度 | MD | ASTM D-1922 | 10 | g/µm | ||
| TD | ASTM D-1922 | 15 | g/µm | |||
| 热性能 | 维卡软化点 | ASTM D-1525 | 105 | ℃ | ||
| 脆化温度 | ASTM D-746 | <-80 | ℃ | |||
| 其它性能 | 薄膜厚度 | ASTM D-746 | 50 | µm | ||