| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.917 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
1.0 |
g/10min |
| 薄膜 |
SecantModulus-1%Secant,MD(40µm,BlownFilm) |
|
ASTMD882 |
150 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(40µm,BlownFilm) |
|
ASTMD882 |
160 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,40µm,BlownFilm) |
|
ASTMD882 |
35.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,40µm,BlownFilm) |
|
ASTMD882 |
25.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,40µm,BlownFilm) |
|
ASTMD882 |
850 |
% |
| 薄膜 |
TensileElongation-TD(Break,40µm,BlownFilm) |
|
ASTMD882 |
840 |
% |
| 薄膜 |
落锤冲击(40µm,吹塑薄膜) |
|
ASTMD1709 |
700 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(40µm,BlownFilm) |
|
ASTMD1922 |
230 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(40µm,BlownFilm) |
|
ASTMD1922 |
790 |
g |
| 光学性能 |
Gloss(60°,40.0µm,BlownFilm) |
|
ASTMD2457 |
84 |
|
| 光学性能 |
雾度(40.0µm,吹塑薄膜) |
|
ASTMD1003 |
7.0 |
% |