LLDPE | FH811U
生产厂家：韩国SK
规格用途
| 规格级别 |
其它 薄膜 其它 |
外观颜色 |
|
| 该料用途 |
重包装用，特殊高强度薄膜。 |
| 备注说明 |
特性：抗张强度、撕裂强度 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-1505 |
0.925 |
g/cm3 |
| 熔体流动速率 |
|
ASTM D-1238 |
0.65 |
g/10min |
| 物理性能 |
薄膜厚度 |
|
|
190 |
µm |
| 机械性能 |
拉伸断裂强度 |
MD |
|
ASTM D-882 |
440 |
Kg/cm2 |
| TD |
|
ASTM D-882 |
410 |
Kg/cm2 |
| 撕裂强度 |
MD |
|
ASTM D-1004 |
130 |
Kg/cm |
| TD |
|
ASTM D-1004 |
125 |
Kg/cm |
| 断裂伸长率 |
MD |
|
ASTM D-882 |
800 |
% |
| TD |
|
ASTM D-882 |
810 |
% |
| 尖头冲击强度 |
|
ASTM D-3420 |
3.7 |
g/μm |
| 拉伸屈服强度 |
MD |
|
ASTM D-882 |
150 |
Kg/cm2 |
| TD |
|
ASTM D-882 |
145 |
Kg/cm2 |
| 抗张模数 |
MD |
|
ASTM D-882 |
2600 |
Kg/cm2 |
| TD |
|
ASTM D-882 |
3500 |
Kg/cm2 |
| 热性能 |
维卡软化点 |
|
ASTM D-1525 |
110 |
℃ |
| 低温脆化温度 |
|
ASTM D-746 |
<-80 |
℃ |
-
-