LLDPE | FH409
生产厂家：韩国SK
规格用途
| 规格级别 |
其它 薄膜 其它 |
外观颜色 |
|
| 该料用途 |
薄膜，重型膜薄 |
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
薄膜厚度 |
|
ASTM D-746 |
50 |
μm |
| 熔融指数 |
|
ASTM D-1238 |
1.0 |
g/10min |
| 密度 |
|
ASTM D-1505 |
0.924 |
g/cm3 |
| 机械性能 |
撕裂强度 |
MD |
|
ASTM D-1992 |
4 |
g/μm |
| TD |
|
ASTM D-1992 |
11 |
g/μm |
| 拉伸强度 |
(断裂点)MD |
|
ASTM D-882 |
453 |
kg/cm2 |
| (断裂点)TD |
|
ASTM D-882 |
370 |
kg/cm2 |
| 拉伸强度 |
(屈服点)MD |
|
ASTM D-882 |
135 |
kg/cm2 |
| (屈服点)TD |
|
ASTM D-882 |
120 |
kg/cm2 |
| 抗冲击强度 |
Spencer |
ASTM D-3420 |
9 |
kg.cm |
| 伸长率 |
MD |
|
ASTM D-882 |
765 |
% |
| TD |
|
ASTM D-882 |
855 |
% |
| 热性能 |
脆化温度 |
|
ASTM D-746 |
＜-70 |
℃ |
| 维卡软化点 |
|
ASTM D-1525 |
102 |
℃ |
| 其它性能 |
添加剂 |
|
SK Method |
A/B |
|
| 雾度 |
|
ASTM D-1003 |
22 |
% |
-
-