| 规格级别 | 吹塑薄膜,流延薄膜 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 0.925 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 2.0 | g/10min | |
| 薄膜 | 膜耐刺穿性 | 20µm | 21.7 | J/cm³ | |
| 薄膜 | 膜耐刺穿性 | 51µm | 22.4 | J/cm³ | |
| 薄膜 | 膜强度 | MD:20µm | ASTMD882 | 88.5 | J/cm³ |
| 薄膜 | 膜强度 | MD:51µm | ASTMD882 | 130 | J/cm³ |
| 薄膜 | 膜强度 | TD:20µm | ASTMD882 | 142 | J/cm³ |
| 薄膜 | 膜强度 | TD:51µm | ASTMD882 | 138 | J/cm³ |
| 薄膜 | 抗张强度 | MD:屈服,20µm | ASTMD882 | 11.7 | MPa |
| 薄膜 | 抗张强度 | MD:屈服,51µm | ASTMD882 | 11.0 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,20µm | ASTMD882 | 10.4 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,51µm | ASTMD882 | 10.4 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,20µm | ASTMD882 | 50.2 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,51µm | ASTMD882 | 48.7 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,20µm | ASTMD882 | 40.5 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,51µm | ASTMD882 | 40.4 | MPa |
| 薄膜 | 伸长率 | MD:断裂,20µm | ASTMD882 | 420 | % |
| 薄膜 | 伸长率 | MD:断裂,51µm | ASTMD882 | 670 | % |
| 薄膜 | 伸长率 | TD:断裂,20µm | ASTMD882 | 800 | % |
| 薄膜 | 伸长率 | TD:断裂,51µm | ASTMD882 | 790 | % |
| 薄膜 | 落锤冲击 | 20µm | ASTMD1709A | 94 | g |
| 薄膜 | 落锤冲击 | 51µm | ASTMD1709A | 180 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:20µm | ASTMD1922 | 160 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:51µm | ASTMD1922 | 650 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:20µm | ASTMD1922 | 580 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:51µm | ASTMD1922 | 960 | g |
| 热性能 | 维卡软化温度 | ASTMD1525 | 108 | °C | |
| 热性能 | 溶融温度（DSC） | 内部方法 | 124 | °C | |
| 光学性能 | 光泽度 | 45°,20.3µm | ASTMD2457 | 93 | |
| 光学性能 | 光泽度 | 45°,50.8µm | ASTMD2457 | 91 | |
| 光学性能 | 雾度 | 20.3µm | ASTMD1003 | 1.2 | % |
| 光学性能 | 雾度 | 50.8µm | ASTMD1003 | 3.7 | % |