| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.925 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
3.7 |
g/10min |
| 机械性能 |
伸长率(断裂) |
|
ASTMD638 |
150 |
% |
| 薄膜 |
薄膜厚度-经测试 |
|
|
25 |
µm |
| 薄膜 |
膜刺穿强度(25µm) |
|
InternalMethod |
0.450 |
J |
| 薄膜 |
割线模量-1%正割,MD(25µm) |
|
ASTMD882 |
155 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(25µm) |
|
ASTMD882 |
154 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,25µm) |
|
ASTMD882 |
8.30 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,25µm) |
|
ASTMD882 |
8.10 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,25µm) |
|
ASTMD882 |
39.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,25µm) |
|
ASTMD882 |
19.0 |
MPa |
| 薄膜 |
伸长率-MD(断裂,25µm) |
|
ASTMD882 |
520 |
% |
| 薄膜 |
TensileElongation-TD(Break,25µm) |
|
ASTMD882 |
680 |
% |
| 薄膜 |
落锤冲击(25µm) |
|
ASTMD1709A |
62 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD(25µm) |
|
ASTMD1922 |
37 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(25µm) |
|
ASTMD1922 |
260 |
g |
| 热性能 |
熔融温度 |
|
DSC |
124 |
°C |
| 光学性能 |
光泽度(45°,25.0µm) |
|
ASTMD2457 |
81 |
|
| 光学性能 |
雾度(25.0µm) |
|
ASTMD1003 |
5.4 |
% |