| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.918 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
2.3 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
38 |
µm |
| 薄膜 |
抗张强度 |
MD:断裂,38µm,挤塑薄膜 |
ASTMD882 |
40.0 |
MPa |
| 薄膜 |
抗张强度 |
TD:断裂,38µm,挤塑薄膜 |
ASTMD882 |
30.0 |
MPa |
| 薄膜 |
伸长率 |
MD:断裂,38µm,挤塑薄膜 |
ASTMD882 |
1300 |
% |
| 薄膜 |
伸长率 |
TD:断裂,38µm,挤塑薄膜 |
ASTMD882 |
1600 |
% |
| 薄膜 |
弯曲模量 |
1%Secant,MD:38µm,CastFilm |
ASTMD882 |
200 |
MPa |
| 薄膜 |
弯曲模量 |
1%Secant,TD:38µm,CastFilm |
ASTMD882 |
230 |
MPa |
| 薄膜 |
落锤冲击1(38µm,铸造薄膜) |
|
ASTMD1709 |
100 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
MD:38µm,铸造薄膜 |
ASTMD1922 |
150 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
TD:38µm,铸造薄膜 |
ASTMD1922 |
190 |
g |
| 薄膜 |
薄膜厚度-经测试 |
|
|
38 |
µm |
| 薄膜 |
抗张强度 |
MD:断裂,38µm,挤塑薄膜 |
ASTMD882 |
40.0 |
MPa |
| 薄膜 |
抗张强度 |
TD:断裂,38µm,挤塑薄膜 |
ASTMD882 |
30.0 |
MPa |
| 薄膜 |
伸长率 |
MD:断裂,38µm,挤塑薄膜 |
ASTMD882 |
1300 |
% |
| 薄膜 |
伸长率 |
TD:断裂,38µm,挤塑薄膜 |
ASTMD882 |
1600 |
% |
| 薄膜 |
弯曲模量 |
1%Secant,MD:38µm,CastFilm |
ASTMD882 |
200 |
MPa |
| 薄膜 |
弯曲模量 |
1%Secant,TD:38µm,CastFilm |
ASTMD882 |
230 |
MPa |
| 薄膜 |
落锤冲击1(38µm,铸造薄膜) |
|
ASTMD1709 |
100 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
MD:38µm,铸造薄膜 |
ASTMD1922 |
150 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度 |
TD:38µm,铸造薄膜 |
ASTMD1922 |
190 |
g |
| 补充信息 |
生物质含量 |
|
ASTMD6866 |
>87 |
% |