| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.919 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.55 |
g/10min |
| 薄膜 |
TensileStrength-MD(Break,100µm,BlownFilm) |
|
ASTMD882 |
40.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,100µm,BlownFilm) |
|
ASTMD882 |
35.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,100µm,BlownFilm) |
|
ASTMD882 |
1000 |
% |
| 薄膜 |
TensileElongation-TD(Break,100µm,BlownFilm) |
|
ASTMD882 |
1300 |
% |
| 薄膜 |
FlexuralModulus-1%Secant,MD(100µm,BlownFilm) |
|
ASTMD790 |
240 |
MPa |
| 薄膜 |
FlexuralModulus-1%Secant,TD(100µm,BlownFilm) |
|
ASTMD790 |
300 |
MPa |
| 薄膜 |
落锤冲击(100µm,吹塑薄膜) |
|
ASTMD1709 |
330 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(100µm,BlownFilm) |
|
ASTMD1922 |
480 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(100µm,BlownFilm) |
|
ASTMD1922 |
2100 |
g |
| 光学性能 |
Gloss(60°,100µm,BlownFilm) |
|
ASTMD2457 |
50 |
|
| 光学性能 |
雾度(100µm,吹塑薄膜) |
|
ASTMD1003 |
25 |
% |