| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.939 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
3.3 |
g/10min |
| 物理性能 |
抗环境应力开裂 |
50°C,2.00mm,10%Igepal,CompressionMolded,F50 |
ASTMD1693 |
145 |
hr |
| 物理性能 |
抗环境应力开裂 |
50°C,2.00mm,100%Igepal,CompressionMolded,F50 |
ASTMD1693 |
>1000 |
hr |
| 机械性能 |
抗张强度(屈服) |
|
ASTMD638 |
21.0 |
MPa |
| 机械性能 |
伸长率(屈服) |
|
ASTMD638 |
14 |
% |
| 机械性能 |
伸长率(断裂) |
|
ASTMD638 |
>1000 |
% |
| 机械性能 |
弯曲模量 |
|
ASTMD790 |
760 |
MPa |
| 冲击性能 |
ImpactStrength |
-40°C,3.17mm,RotationalMolded |
ARM |
82 |
J |
| 冲击性能 |
ImpactStrength |
-40°C,6.34mm,RotationalMolded |
ARM |
228 |
J |
| 热性能 |
载荷下热变形温度(0.45MPa,未退火) |
|
ASTMD648 |
60.0 |
°C |
| 热性能 |
载荷下热变形温度(1.8MPa,未退火) |
|
ASTMD648 |
41.0 |
°C |
| 热性能 |
熔融峰值温度 |
|
ASTMD3418 |
127 |
°C |
| 热性能 |
氧感应时间 |
|
ASTMD3895 |
>100 |
min |