| 规格级别 | 高光滑性,高抗结块性,光学性能,丁烯共聚单体 | 外观颜色 | |
| 该料用途 | 袋子,包装,片材,薄膜 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.926 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 6.0 | g/10min | |
| 机械性能 | 摩擦系数 | ASTMD1894 | 0.11 | ||
| 薄膜 | 薄膜厚度-经测试 | 30 | µm | ||
| 薄膜 | 抗张强度 | MD:断裂,30µm | ASTMD882 | 30.0 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,30µm | ASTMD882 | 18.0 | MPa |
| 薄膜 | 伸长率 | MD:断裂,30µm | ASTMD882 | 900 | % |
| 薄膜 | 伸长率 | TD:断裂,30µm | ASTMD882 | 800 | % |
| 薄膜 | 落锤冲击2(30µm) | ASTMD1709 | 75 | g | |
| 薄膜 | ElmendorfTearStrength | MD:30.0µm | ASTMD1922 | 44.1 | kN/m |
| 薄膜 | ElmendorfTearStrength | TD:30.0µm | ASTMD1922 | 98.1 | kN/m |
| 薄膜 | 阻塞力(30.0µm) | ASTMD3354 | 69.0 | g/100cm² | |
| 薄膜 | 薄膜厚度-经测试 | 30 | µm | ||
| 薄膜 | 抗张强度 | MD:断裂,30µm | ASTMD882 | 30.0 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,30µm | ASTMD882 | 18.0 | MPa |
| 薄膜 | 伸长率 | MD:断裂,30µm | ASTMD882 | 900 | % |
| 薄膜 | 伸长率 | TD:断裂,30µm | ASTMD882 | 800 | % |
| 薄膜 | 落锤冲击2(30µm) | ASTMD1709 | 75 | g | |
| 薄膜 | ElmendorfTearStrength | MD:30.0µm | ASTMD1922 | 44.1 | kN/m |
| 薄膜 | ElmendorfTearStrength | TD:30.0µm | ASTMD1922 | 98.1 | kN/m |
| 薄膜 | 阻塞力(30.0µm) | ASTMD3354 | 69.0 | g/100cm² | |
| 热性能 | 脆化温度 | ASTMD746 | <-70.0 | °C | |
| 热性能 | 维卡软化温度 | ASTMD1525 | 104 | °C | |
| 光学性能 | 光泽度(45°,30.0µm) | ASTMD2457 | 110 | ||
| 光学性能 | 透明度(30.0µm) | ASTMD1746 | 72.0 | ||
| 光学性能 | 雾度(30.0µm) | ASTMD1003 | 6.0 | % | |