| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.925 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 1.0 | g/10min | |
| 机械性能 | 摩擦系数(吹塑薄膜) | ASTMD1894 | 0.150.13 | ||
| 薄膜 | 薄膜厚度-经测试 | 2850 | µm | ||
| 薄膜 | 割线模量 | 2%正割,MD:28µm | ASTMD882 | 210 | MPa |
| 薄膜 | 割线模量 | 2%正割,MD:50µm | ASTMD882 | 220 | MPa |
| 薄膜 | 割线模量 | 2%正割,TD:28µm | ASTMD882 | 220 | MPa |
| 薄膜 | 割线模量 | 2%正割,TD:50µm | ASTMD882 | 240 | MPa |
| 薄膜 | 抗张强度 | MD:屈服,28µm | ASTMD882 | 9.00 | MPa |
| 薄膜 | 抗张强度 | MD:屈服,50µm | ASTMD882 | 10.0 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,28µm | ASTMD882 | 12.0 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,50µm | ASTMD882 | 12.0 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,28µm | ASTMD882 | 28.0 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,50µm | ASTMD882 | 34.0 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,28µm | ASTMD882 | 24.0 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,50µm | ASTMD882 | 30.0 | MPa |
| 薄膜 | 伸长率 | MD:断裂,28µm | ASTMD882 | 750 | % |
| 薄膜 | 伸长率 | MD:断裂,50µm | ASTMD882 | 1000 | % |
| 薄膜 | 伸长率 | TD:断裂,28µm | ASTMD882 | 800 | % |
| 薄膜 | 伸长率 | TD:断裂,50µm | ASTMD882 | 1000 | % |
| 薄膜 | 落锤冲击 | 28µm,吹塑薄膜 | ASTMD1709 | 130 | g |
| 薄膜 | 落锤冲击 | 50µm,吹塑薄膜 | ASTMD1709 | 240 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:28µm | ASTMD1922 | 310 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:50µm | ASTMD1922 | 590 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:28µm | ASTMD1922 | 510 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:50µm | ASTMD1922 | 980 | g |
| 薄膜 | 薄膜厚度-经测试 | 2850 | µm | ||
| 薄膜 | 割线模量 | 2%正割,MD:28µm | ASTMD882 | 210 | MPa |
| 薄膜 | 割线模量 | 2%正割,MD:50µm | ASTMD882 | 220 | MPa |
| 薄膜 | 割线模量 | 2%正割,TD:28µm | ASTMD882 | 220 | MPa |
| 薄膜 | 割线模量 | 2%正割,TD:50µm | ASTMD882 | 240 | MPa |
| 薄膜 | 抗张强度 | MD:屈服,28µm | ASTMD882 | 9.00 | MPa |
| 薄膜 | 抗张强度 | MD:屈服,50µm | ASTMD882 | 10.0 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,28µm | ASTMD882 | 12.0 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,50µm | ASTMD882 | 12.0 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,28µm | ASTMD882 | 28.0 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,50µm | ASTMD882 | 34.0 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,28µm | ASTMD882 | 24.0 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,50µm | ASTMD882 | 30.0 | MPa |
| 薄膜 | 伸长率 | MD:断裂,28µm | ASTMD882 | 750 | % |
| 薄膜 | 伸长率 | MD:断裂,50µm | ASTMD882 | 1000 | % |
| 薄膜 | 伸长率 | TD:断裂,28µm | ASTMD882 | 800 | % |
| 薄膜 | 伸长率 | TD:断裂,50µm | ASTMD882 | 1000 | % |
| 薄膜 | 落锤冲击 | 28µm,吹塑薄膜 | ASTMD1709 | 130 | g |
| 薄膜 | 落锤冲击 | 50µm,吹塑薄膜 | ASTMD1709 | 240 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:28µm | ASTMD1922 | 310 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:50µm | ASTMD1922 | 590 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:28µm | ASTMD1922 | 510 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:50µm | ASTMD1922 | 980 | g |
| 光学性能 | 光泽度 | 28.0µm,吹塑薄膜 | ASTMD2457 | 72 | |
| 光学性能 | 光泽度 | 50.0µm,吹塑薄膜 | ASTMD2457 | 74 | |
| 光学性能 | 雾度 | 28.0µm,吹塑薄膜 | ASTMD1003 | 8.0 | % |
| 光学性能 | 雾度 | 50.0µm,吹塑薄膜 | ASTMD1003 | 10 | % |