| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.19 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率） |
230°C/3.8kg |
ASTMD1238 |
3.0 |
g/10min |
| 物理性能 |
熔流率（熔体流动速率） |
260°C/5.0kg |
ASTMD1238 |
14 |
g/10min |
| 物理性能 |
收缩率-流动 |
|
ASTMD955 |
0.40to0.60 |
% |
| 机械性能 |
拉伸模量(3.20mm,注塑) |
|
ASTMD638 |
2780 |
MPa |
| 机械性能 |
TensileStrength(Yield,3.20mm,InjectionMolded) |
|
ASTMD638 |
67.0 |
MPa |
| 机械性能 |
TensileStrength(Break,3.20mm,InjectionMolded) |
|
ASTMD638 |
62.0 |
MPa |
| 机械性能 |
TensileElongation(Yield,3.20mm,InjectionMolded) |
|
ASTMD638 |
5.0 |
% |
| 机械性能 |
TensileElongation(Break,3.20mm,InjectionMolded) |
|
ASTMD638 |
71 |
% |
| 机械性能 |
FlexuralModulus(3.20mm,InjectionMolded) |
|
ASTMD790 |
2560 |
MPa |
| 机械性能 |
FlexuralStrength(3.20mm,InjectionMolded) |
|
ASTMD790 |
104 |
MPa |
| 冲击性能 |
悬壁梁缺口冲击强度 |
-30°C,3.20mm,注塑 |
ASTMD256 |
130 |
J/m |
| 冲击性能 |
悬壁梁缺口冲击强度 |
0°C,3.20mm,InjectionMolded |
ASTMD256 |
350 |
J/m |
| 冲击性能 |
悬壁梁缺口冲击强度 |
23°C,3.20mm,注塑 |
ASTMD256 |
740 |
J/m |
| 硬度 |
洛氏硬度(R级,3.20mm,注塑) |
|
ASTMD785 |
121 |
|
| 热性能 |
载荷下热变形温度(0.45MPa,未退火) |
|
ASTMD648 |
98.0 |
°C |
| 热性能 |
载荷下热变形温度(1.8MPa,未退火) |
|
ASTMD648 |
86.0 |
°C |
| 热性能 |
维卡软化温度 |
-- |
ASTMD15252 |
104 |
°C |
| 热性能 |
维卡软化温度 |
-- |
ASTMD15253 |
114 |
°C |
| 热性能 |
CLTE-Flow(-40to180°C) |
|
ASTMD696 |
7.3E-5 |
cm/cm/°C |
| 热性能 |
CLTE-Transverse(-40to180°C) |
|
ASTMD696 |
6.7E-5 |
cm/cm/°C |
| 可燃性 |
UL阻燃等级5 |
1.5mm |
UL94 |
V-0 |
|
| 可燃性 |
UL阻燃等级5 |
2.0mm |
UL94 |
5VB |
|
| 可燃性 |
UL阻燃等级5 |
2.5mm |
UL94 |
5VA |
|
| 可燃性 |
极限氧指数 |
|
ASTMD2863 |
33 |
% |