| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.17 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率） |
230°C/3.8kg |
ASTMD1238 |
17 |
g/10min |
| 物理性能 |
熔流率（熔体流动速率） |
260°C/5.0kg |
ASTMD1238 |
75 |
g/10min |
| 物理性能 |
收缩率-流动 |
|
ASTMD955 |
0.40to0.60 |
% |
| 机械性能 |
TensileStrength(Yield,3.20mm,InjectionMolded) |
|
ASTMD638 |
62.1 |
MPa |
| 机械性能 |
TensileStrength(Break,3.20mm,InjectionMolded) |
|
ASTMD638 |
46.2 |
MPa |
| 机械性能 |
TensileElongation(Yield,3.20mm,InjectionMolded) |
|
ASTMD638 |
4.0 |
% |
| 机械性能 |
TensileElongation(Break,3.20mm,InjectionMolded) |
|
ASTMD638 |
50 |
% |
| 机械性能 |
FlexuralModulus(3.20mm,InjectionMolded) |
|
ASTMD790 |
2830 |
MPa |
| 机械性能 |
FlexuralStrength(3.20mm,InjectionMolded) |
|
ASTMD790 |
97.9 |
MPa |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C,3.20mm,注塑) |
|
ASTMD256 |
640 |
J/m |
| 热性能 |
载荷下热变形温度(0.45MPa,未退火) |
|
ASTMD648 |
93.9 |
°C |
| 热性能 |
载荷下热变形温度(1.8MPa,未退火) |
|
ASTMD648 |
82.2 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD15252 |
108 |
°C |
| 可燃性 |
FlameRating3(1.5mm) |
|
UL94 |
V-0 |
|
| 可燃性 |
极限氧指数3 |
|
ASTMD2863 |
29 |
% |