| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-792 |
0.92 |
g/m3 |
| 熔体流动速率 |
190℃/2.16kg |
ISO 1133 |
25 |
g/10min |
| 物理性能 |
成型收缩率 |
|
ASTM D-955 |
2.4 |
% |
| 机械性能 |
环境开裂应力 |
50℃，100% Antarox，Compression Molded |
ASTM D-1693 |
6.7 |
hr |
| 环境开裂应力 |
50℃，100% Antarox，Injection Molded |
ASTM D-1693 |
1.2 |
hr |
| 拉伸模量 |
Compression Molded |
ASTM D-638 |
256 |
MPa |
| 拉伸模量 |
Injection Molded |
ASTM D-638 |
155 |
MPa |
| 拉伸屈服强度 |
Compression Molded |
ASTM D-638 |
12 |
MPa |
| 拉伸屈服强度 |
Injection Molded |
ASTM D-638 |
7.1 |
MPa |
| 拉伸断裂强度 |
Injection Molded |
ASTM D-638 |
>11.6 |
MPa |
| 拉伸断裂伸长率 |
Injection Molded |
ASTM D-638 |
> 870 |
% |
| IZOD缺口冲击强度 |
-20℃，Injection Molded |
ASTM D-256 |
No Break |
|
| IZOD缺口冲击强度 |
-40℃，Injection Molded |
ASTM D-256 |
90 |
kJ/m2 |
| IZOD缺口冲击强度 |
23℃，Injection Molded |
ASTM D-256 |
No Break |
|
| 拉伸冲击强度 |
Compression Molded |
ISO 8256 |
105 |
kJ/m2 |
| 邵氏硬度 |
Shore D，Compression Molded |
ASTM D-2240 |
48 |
|
| 热性能 |
维卡软化点 |
|
ASTM D-1525 |
92 |
℃ |