| 规格级别 | 其它 其它 吹塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 0.920 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 1.0 |
g/10 min
|
|
| 薄膜 |
膜耐刺穿性
|
20 µm
|
17.5 |
J/cm³
|
|
|
51 µm
|
9.27 |
J/cm³
|
|||
|
膜强度
|
MD : 20 µm
|
ASTM D882 | 137 |
J/cm³
|
|
|
MD : 51 µm
|
ASTM D882 | 127 |
J/cm³
|
||
|
TD : 20 µm
|
ASTM D882 | 126 |
J/cm³
|
||
|
TD : 51 µm
|
ASTM D882 | 145 |
J/cm³
|
||
|
割线模量
|
2% 正割, MD : 20 µm
|
ASTM D882 | 216 |
MPa
|
|
|
2% 正割, MD : 51 µm
|
ASTM D882 | 208 |
MPa
|
||
|
2% 正割, TD : 20 µm
|
ASTM D882 | 276 |
MPa
|
||
|
2% 正割, TD : 51 µm
|
ASTM D882 | 259 |
MPa
|
||
|
抗张强度
|
MD : 屈服, 20 µm
|
ASTM D882 | 11.1 |
MPa
|
|
|
MD : 屈服, 51 µm
|
ASTM D882 | 10.9 |
MPa
|
||
|
TD : 屈服, 20 µm
|
ASTM D882 | 7.89 |
MPa
|
||
|
TD : 屈服, 51 µm
|
ASTM D882 | 11.5 |
MPa
|
||
|
MD : 断裂, 20 µm
|
ASTM D882 | 53.6 |
MPa
|
||
|
MD : 断裂, 51 µm
|
ASTM D882 | 41.4 |
MPa
|
||
|
TD : 断裂, 20 µm
|
ASTM D882 | 41.7 |
MPa
|
||
|
TD : 断裂, 51 µm
|
ASTM D882 | 47.5 |
MPa
|
||
|
伸长率
|
MD : 断裂, 20 µm
|
ASTM D882 | 670 | % | |
|
MD : 断裂, 51 µm
|
ASTM D882 | 670 | % | ||
|
TD : 断裂, 20 µm
|
ASTM D882 | 730 | % | ||
|
TD : 断裂, 51 µm
|
ASTM D882 | 820 | % | ||
| 落锤冲击 |
20 µm
|
ASTM D1709A | 200 |
g
|
|
|
51 µm
|
ASTM D1709A | 330 |
g
|
||
| 埃尔曼多夫抗撕强度 |
MD : 20 µm
|
ASTM D1922 | 480 |
g
|
|
|
MD : 51 µm
|
ASTM D1922 | 980 |
g
|
||
|
TD : 20 µm
|
ASTM D1922 | 620 |
g
|
||
|
TD : 51 µm
|
ASTM D1922 | 1200 |
g
|
||
| 热性能 |
维卡软化温度
|
ASTM D1525 | 106 | ℃ | |
|
熔融温度
|
DSC | 121 | ℃ | ||
| 光学性能 | 光泽度 |
45°, 20.3 µm
|
ASTM D2457 | 75 | |
|
45°, 50.8 µm
|
ASTM D2457 | 72 | |||
| 雾度 |
20.3 µm
|
ASTM D1003 | 6.3 | % | |
|
50.8 µm
|
ASTM D1003 | 9.7 | % | ||