| 规格级别 | 其它 薄膜 吹塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 超高抗冲击性、低密度、高光滑性、 高抗结块性、高强度、良好的热封性、良好的撕裂强度 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D1505 | 0.918 |
g/cm³
|
|
| 熔流率 | 190°C/2.16 kg | ASTM D1238 | 1.0 |
g/10 min
|
|
薄膜 |
薄膜厚度 | 经测试 | 38 |
µm
|
|
| 割线模量 |
1% 正割, MD: 38 µm, 吹塑薄膜
|
ASTM D882 | 157 |
MPa
|
|
|
1% 正割, TD: 38 µm, 吹塑薄膜
|
ASTM D882 | 196 |
MPa
|
||
| 抗张强度 |
MD: 屈服, 38 µm, 吹塑薄膜
|
ASTM D882 | 9.81 |
MPa
|
|
|
TD: 屈服, 38 µm, 吹塑薄膜
|
ASTM D882 | 10.8 |
MPa
|
||
|
MD: 断裂, 38 µm, 吹塑薄膜
|
ASTM D882 | 49.0 |
MPa
|
||
|
TD: 断裂, 38 µm, 吹塑薄膜
|
ASTM D882 | 44.1 |
MPa
|
||
| 伸长率 |
MD: 断裂, 38 µm, 吹塑薄膜
|
ASTM D882 | 620 | % | |
|
TD: 断裂, 38 µm, 吹塑薄膜
|
ASTM D882 | 810 | % | ||
| 落锤冲击 | 38 µm, 吹塑薄膜 | ASTM D1709 | 610 |
g
|
|
| 埃尔曼多夫抗撕强度 |
MD: 38 µm, 吹塑薄膜
|
ASTM D1922 | 460 |
g
|
|
|
TD: 38 µm, 吹塑薄膜
|
ASTM D1922 | 760 |
g
|
||
| 热性能 |
脆化温度 | ASTM D746 | -70.0 |
°C
|
|
| 维卡软化温度 | ASTM D1525 | 93.0 |
°C
|
||
| 熔融温度 | ASTM D1525 | 121 |
°C
|
||