| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 0.917 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 3.3 |
g/10 min
|
|
| 薄膜 | 薄膜厚度 |
经测试
|
23 |
µm
|
|
|
抗张强度
|
MD : 屈服, 23 µm, 挤塑薄膜
|
ASTM D882 | 6.20 |
MPa
|
|
|
TD : 屈服, 23 µm, 挤塑薄膜
|
ASTM D882 | 5.50 |
MPa
|
||
|
MD : 断裂, 23 µm, 挤塑薄膜
|
ASTM D882 | 38.0 |
MPa
|
||
|
TD : 断裂, 23 µm, 挤塑薄膜
|
ASTM D882 | 21.0 |
MPa
|
||
|
伸长率
|
MD : 断裂, 23 µm, 挤塑薄膜
|
ASTM D882 | 500 | % | |
|
TD : 断裂, 23 µm, 挤塑薄膜
|
ASTM D882 | 780 | % | ||
| 落锤冲击 | 25 µm, 铸造薄膜 | ASTM D1709 | 140 |
g
|
|
| 埃尔曼多夫抗撕强度 |
MD : 23 µm, 铸造薄膜
|
ASTM D1922 | 320 |
g
|
|
|
TD : 23 µm, 铸造薄膜
|
ASTM D1922 | 530 |
g
|
||
| 薄膜拉伸性能 - 最大拉伸到穿透 | 23.0 µm | Internal Method | 160 | % | |
| 薄膜拉伸性能 - 最大伸长率 | 23.0 µm | Internal Method | 260 | % | |
| 光学性能 | 光泽度 | 45°, 23.0 µm, 铸造薄膜 | ASTM D2457 | 93 | |
| 雾度 | 23.0 µm, 铸造薄膜 | ASTM D1003 | 0.60 | % | |