| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 0.926 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 1.0 |
g/10 min
|
|
| 薄膜 | 薄膜厚度 |
经测试
|
38 |
µm
|
|
| 膜刺穿强度 | 38µm | Internal Method | 3.06 |
J/cm³
|
|
|
膜强度
|
MD : 38 µm
|
ASTM D882 | 128 |
J/cm³
|
|
|
TD : 38 µm
|
ASTM D882 | 140 |
J/cm³
|
||
|
割线模量
|
2% 正割, MD : 38 µm
|
ASTM D882 | 235 |
MPa
|
|
|
2% 正割, TD : 38 µm
|
ASTM D882 | 281 |
MPa
|
||
|
抗张强度
|
MD : 屈服, 38 µm
|
ASTM D882 | 13.2 |
MPa
|
|
|
TD : 屈服,38 µm
|
ASTM D882 | 14.8 |
MPa
|
||
|
MD : 断裂, 38 µm
|
ASTM D882 | 47.8 |
MPa
|
||
|
TD : 断裂, 38 µm
|
ASTM D882 | 42.3 |
MPa
|
||
|
伸长率
|
MD : 断裂, 38 µm
|
ASTM D882 | 630 | % | |
|
TD : 断裂, 38 µm
|
ASTM D882 | 740 | % | ||
| 落锤冲击 | 25 µm | ASTM D1709 | 220 |
g
|
|
| 埃尔曼多夫抗撕强度 |
MD : 38 µm
|
ASTM D1922 | 250 |
g
|
|
|
TD : 38µm
|
ASTM D1922 | 590 |
g
|
||
| 热性能 |
维卡软化温度
|
ASTM D1525 | 112 | ℃ | |
| 溶融温度 | DSC | Internal Method | 121 | ℃ | |
| 光学性能 | 光泽度 | 45°, 38.1 µm | ASTM D2457 | 80 | |
| 雾度 | 38.1 µm | ASTM D1003 | 9.0 | % | |