| 规格级别 | 其它 其它 吹塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 0.920 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 1.0 |
g/10 min
|
|
| 薄膜 | 薄膜厚度 |
经测试
|
25 |
µm
|
|
| 膜刺穿强度 | Internal Method | 5.31 |
J
|
||
|
膜刺穿力
|
Internal Method | 62.3 |
N
|
||
|
膜耐刺穿性
|
Internal Method | 26.1 |
J/cm³
|
||
|
膜强度
|
MD
|
ASTM D882 | 118 |
J/cm³
|
|
|
TD
|
ASTM D882 | 129 |
J/cm³
|
||
|
割线模量
|
1% 正割, MD
|
ASTM D882 | 237 |
MPa
|
|
| 2% 正割, MD | ASTM D882 | 205 |
MPa
|
||
|
1% 正割, TD
|
ASTM D882 | 275 |
MPa
|
||
|
2% 正割, TD
|
ASTM D882 | 232 |
MPa
|
||
|
抗张强度
|
MD : 屈服
|
ASTM D882 | 11.4 |
MPa
|
|
|
TD : 屈服
|
ASTM D882 | 11.9 |
MPa
|
||
|
MD : 断裂
|
ASTM D882 | 47.4 |
MPa
|
||
|
TD : 断裂
|
ASTM D882 | 40.6 |
MPa
|
||
|
伸长率
|
MD : 断裂
|
ASTM D882 | 600 | % | |
|
TD : 断裂
|
ASTM D882 | 740 | % | ||
| 落锤冲击 | 25 µm | ASTM D1709 | 220 |
g
|
|
| 埃尔曼多夫抗撕强度 |
MD : 25 µm
|
ASTM D1922 | 370 |
g
|
|
|
TD : 25 µm
|
ASTM D1922 | 630 |
g
|
||
| 热性能 |
维卡软化温度
|
ASTM D1525 | 106 | ℃ | |
| 溶融温度 | DSC | Internal Method | 119 | ℃ | |
| 光学性能 | 光泽度 | 20°, 24.9 µm | ASTM D2457 | 60 | |
| 雾度 | 24.9 µm | ASTM D1003 | 10 | % | |