| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 0.933 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 2.5 |
g/10 min
|
|
| 薄膜 |
膜耐刺穿性
|
Internal Method | 10.3 |
J/cm³
|
|
|
膜强度
|
MD
|
ASTM D882 | 324 |
J/cm³
|
|
|
TD
|
ASTM D882 | 308 |
J/cm³
|
||
|
抗张强度
|
MD : 屈服
|
ASTM D882 | 16.9 |
MPa
|
|
|
TD : 屈服
|
ASTM D882 | 17.6 |
MPa
|
||
|
MD : 断裂
|
ASTM D882 | 59.2 |
MPa
|
||
|
TD : 断裂
|
ASTM D882 | 39.9 |
MPa
|
||
|
伸长率
|
MD : 断裂
|
ASTM D882 | 620 | % | |
|
TD : 断裂
|
ASTM D882 | 750 | % | ||
|
落锤冲击
|
ASTM D1709A | 57 |
g
|
||
| 埃尔曼多夫抗撕强度 |
MD
|
ASTM D1922 | 83 |
g
|
|
|
TD
|
ASTM D1922 | 290 |
g
|
||
| 热性能 |
维卡软化温度
|
ASTM D1525 | 119 | ℃ | |
| 溶融温度 | DSC | Internal Method | 125 | ℃ | |
| 光学性能 | 光泽度 | 45° | ASTM D2457 | 90 | |
|
雾度
|
ASTM D1003 | 2.6 | % | ||