| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 0.918 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 2.0 |
g/10 min
|
|
| 薄膜 | 薄膜厚度 |
经测试
|
25 |
µm
|
|
| 膜刺穿强度 | 25 µm | Internal Method | 48.9 |
N
|
|
| 膜耐刺穿性 |
25 µm
|
Internal Method | 9.02 |
J/cm³
|
|
|
割线模量
|
2% 正割, MD : 25 µm
|
ASTM D882 | 149 |
MPa
|
|
|
2% 正割, TD : 25 µm
|
ASTM D882 | 147 |
MPa
|
||
|
抗张强度
|
MD : 屈服, 25 µm
|
ASTM D882 | 10.7 |
MPa
|
|
|
TD : 屈服, 25 µm
|
ASTM D882 | 8.94 |
MPa
|
||
|
MD : 断裂, 25 µm
|
ASTM D882 | 39.6 |
MPa
|
||
|
TD : 断裂, 25 µm
|
ASTM D882 | 20.6 |
MPa
|
||
|
伸长率
|
MD : 断裂, 25 µm
|
ASTM D882 | 450 | % | |
|
TD : 断裂, 25 µm
|
ASTM D882 | 680 | % | ||
| 落锤冲击 | 25 µm | ASTM D1709 | 66 |
g
|
|
| 埃尔曼多夫抗撕强度 |
MD : 25 µm
|
ASTM D1922 | 37 |
g
|
|
|
TD : 25 µm
|
ASTM D1922 | 370 |
g
|
||
| 薄膜拉伸性能 | 最大伸长率 | Internal Method | 230 | % | |
| 热性能 |
维卡软化温度
|
ASTM D1525 | 96.1 | ℃ | |
| 溶融温度 | DSC | Internal Method | 116 | ℃ | |
| 光学性能 | 光泽度 | 20°, 25.4 µm | ASTM D2457 | 151 | |
| 雾度 | 25.4 µm | ASTM D1003 | 0.56 | % | |