LLDPE | 1210
生产厂家：美国陶氏
规格用途
| 规格级别 |
其它 薄膜 其它 |
外观颜色 |
|
| 该料用途 |
工业，食品和特殊的包装 |
| 备注说明 |
良好热封性、加工性、含滑爽剂 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-792 |
0.9190 |
g/cc |
| 机械性能 |
屈服拉伸强度 |
MD |
|
ASTM D-882 |
10.3 |
MPa |
| TD |
|
ASTM D-882 |
11.1 |
MPa |
| 断裂拉伸强度 |
MD |
|
ASTM D-882 |
31.7 |
MPa |
| TD |
|
ASTM D-882 |
25.1 |
MPa |
| 刺穿强度 |
|
ASTM DOW |
8.2 |
J/cm3 |
| Dart 冲击强度 |
|
ASTM D-1709 |
<100 |
g |
| 热性能 |
维卡软化点 |
|
ASTM D-1525 |
101 |
℃ |
| 其它性能 |
断裂伸长率 |
MD |
|
ASTM D-882 |
658 |
% |
| TD |
|
ASTM D-882 |
714 |
% |
| 熔融指数 |
|
ASTM D-1238 |
1.00 |
g/10min |
| 熔点 |
|
ASTM DOW |
108 |
℃ |
| 抗撕裂性 |
MD |
|
ASTM D-1992 |
106 |
g |
| TD |
|
ASTM D-1992 |
256 |
g |
| 光泽度 |
20° |
ASTM D-2457 |
69 |
|
| 拉伸模量 |
MD |
|
ASTM D-882 |
183.3 |
MPa |
| TD |
|
ASTM D-882 |
217.4 |
MPa |
| 韧性 |
MD |
|
ASTM D-882 |
102.6 |
J/cm3 |
| TD |
|
ASTM D-882 |
98.1 |
J/cm3 |
| TD |
|
ASTM D-882 |
98.1 |
J/cm3 |
| 透明度 |
|
ASTM D-1746 |
95 |
|
| 雾度 |
|
ASTM D-1003 |
10.8 |
% |
-
-