| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 0.922 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 0.27 | g/10min | |
| 薄膜 | 薄膜厚度-经测试 | 35 | µm | ||
| 薄膜 | 膜刺穿力(35µm) | ASTMD3420 | 14.1 | N | |
| 薄膜 | 抗张强度 | MD:断裂,35µm | ASTMD882 | 20.0 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,35µm | ASTMD882 | 19.0 | MPa |
| 薄膜 | 伸长率 | MD:断裂,100µm | ASTMD882 | 35 | % |
| 薄膜 | 伸长率 | TD:断裂,35µm | ASTMD882 | 500 | % |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:35µm | ASTMD1922 | 200 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:35µm | ASTMD1922 | 250 | g |
| 薄膜 | ImpactResistance,Film | ASTMD1709 | 280 | J/cm | |
| 薄膜 | Toughness,Film | MD | ASTMD882 | 48.0 | MPa |
| 薄膜 | Toughness,Film | TD | ASTMD882 | 62.0 | MPa |
| 薄膜 | 薄膜厚度-经测试 | 35 | µm | ||
| 薄膜 | 膜刺穿力(35µm) | ASTMD3420 | 14.1 | N | |
| 薄膜 | 抗张强度 | MD:断裂,35µm | ASTMD882 | 20.0 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,35µm | ASTMD882 | 19.0 | MPa |
| 薄膜 | 伸长率 | MD:断裂,100µm | ASTMD882 | 35 | % |
| 薄膜 | 伸长率 | TD:断裂,35µm | ASTMD882 | 500 | % |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:35µm | ASTMD1922 | 200 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:35µm | ASTMD1922 | 250 | g |
| 薄膜 | ImpactResistance,Film | ASTMD1709 | 280 | J/cm | |
| 薄膜 | Toughness,Film | MD | ASTMD882 | 48.0 | MPa |
| 薄膜 | Toughness,Film | TD | ASTMD882 | 62.0 | MPa |
| 光学性能 | 透射率(35.0µm) | ASTMD1003 | 66.0 | % | |
| 光学性能 | 雾度(35.0µm) | ASTMD1003 | 31 | % | |