| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.919 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 2.0 | g/10min | |
| 薄膜 | 薄膜厚度-经测试 | 38 | µm | ||
| 薄膜 | 割线模量 | 1%正割,MD:38µm | ASTMD882 | 175 | MPa |
| 薄膜 | 割线模量 | 1%正割,TD:38µm | ASTMD882 | 205 | MPa |
| 薄膜 | 抗张强度 | MD:屈服,38µm | ASTMD882 | 10.0 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,38µm | ASTMD882 | 10.0 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,38µm | ASTMD882 | 25.0 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,38µm | ASTMD882 | 19.0 | MPa |
| 薄膜 | 伸长率 | MD:断裂,38µm | ASTMD882 | 350 | % |
| 薄膜 | 伸长率 | TD:断裂,38µm | ASTMD882 | 600 | % |
| 薄膜 | 落锤冲击(38µm) | ASTMD1709A | 85 | g | |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:38µm | ASTMD1922 | 580 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:38µm | ASTMD1922 | 120 | g |
| 薄膜 | 薄膜厚度-经测试 | 38 | µm | ||
| 薄膜 | 割线模量 | 1%正割,MD:38µm | ASTMD882 | 175 | MPa |
| 薄膜 | 割线模量 | 1%正割,TD:38µm | ASTMD882 | 205 | MPa |
| 薄膜 | 抗张强度 | MD:屈服,38µm | ASTMD882 | 10.0 | MPa |
| 薄膜 | 抗张强度 | TD:屈服,38µm | ASTMD882 | 10.0 | MPa |
| 薄膜 | 抗张强度 | MD:断裂,38µm | ASTMD882 | 25.0 | MPa |
| 薄膜 | 抗张强度 | TD:断裂,38µm | ASTMD882 | 19.0 | MPa |
| 薄膜 | 伸长率 | MD:断裂,38µm | ASTMD882 | 350 | % |
| 薄膜 | 伸长率 | TD:断裂,38µm | ASTMD882 | 600 | % |
| 薄膜 | 落锤冲击(38µm) | ASTMD1709A | 85 | g | |
| 薄膜 | 埃尔曼多夫抗撕强度 | MD:38µm | ASTMD1922 | 580 | g |
| 薄膜 | 埃尔曼多夫抗撕强度 | TD:38µm | ASTMD1922 | 120 | g |
| 光学性能 | 光泽度(45°,25.0µm,吹塑薄膜) | ASTMD2457 | 10 | ||
| 光学性能 | 雾度(25.0µm,吹塑薄膜) | ASTMD1003 | 1.5 | % | |