| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.918 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.18 |
g/10min |
| 物理性能 |
抗环境应力开裂(100%Igepal,F0) |
|
ASTMD1693 |
168 |
hr |
| 机械性能 |
抗张强度(屈服) |
|
ASTMD638 |
9.65 |
MPa |
| 机械性能 |
抗张强度(断裂) |
|
ASTMD638 |
17.9 |
MPa |
| 机械性能 |
伸长率(屈服) |
|
ASTMD638 |
100 |
% |
| 机械性能 |
伸长率(断裂) |
|
ASTMD638 |
750 |
% |
| 薄膜 |
薄膜厚度-经测试 |
|
|
51 |
µm |
| 薄膜 |
TensileStrength-MD(Yield,51µm,BlownFilm) |
|
ASTMD882 |
20.7 |
MPa |
| 薄膜 |
伸长率-MD(断裂,51µm,吹塑薄膜) |
|
ASTMD882 |
300 |
% |
| 薄膜 |
TensileElongation-TD(Break,51µm,BlownFilm) |
|
ASTMD882 |
450 |
% |
| 薄膜 |
DartDropImpact(51µm,BlownFilm) |
|
ASTMD1709 |
220 |
g |
| 硬度 |
肖氏硬度(邵氏D) |
|
ASTMD2240 |
42 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-75.0 |
°C |