| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.925 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
1.2 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
25 |
µm |
| 薄膜 |
割线模量-1%正割,MD(25µm) |
|
ASTMD882 |
221 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(25µm) |
|
ASTMD882 |
262 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,25µm) |
|
ASTMD882 |
23.1 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,25µm) |
|
ASTMD882 |
19.3 |
MPa |
| 薄膜 |
伸长率-MD(断裂,25µm) |
|
ASTMD882 |
330 |
% |
| 薄膜 |
TensileElongation-TD(Break,25µm) |
|
ASTMD882 |
500 |
% |
| 薄膜 |
落锤冲击(25µm) |
|
ASTMD1709 |
85 |
g |
| 光学性能 |
Gloss(60°,25.4µm) |
|
ASTMD2457 |
100 |
|
| 光学性能 |
雾度(25.4µm) |
|
ASTMD1003 |
7.5 |
% |