| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.925 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.60 |
g/10min |
| 薄膜 |
SecantModulus-1%Secant,MD |
32µm,BlownFilm |
ASTMD882 |
248 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,MD |
50µm,吹塑薄膜 |
ASTMD882 |
228 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD |
32µm,BlownFilm |
ASTMD882 |
290 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD |
50µm,吹塑薄膜 |
ASTMD882 |
269 |
MPa |
| 薄膜 |
抗张强度-MD |
Yield,32µm,BlownFilm |
ASTMD882 |
11.0 |
MPa |
| 薄膜 |
抗张强度-MD |
屈服,51µm,吹塑薄膜 |
ASTMD882 |
11.0 |
MPa |
| 薄膜 |
TensileStrength-TD |
Yield,32µm,BlownFilm |
ASTMD882 |
11.7 |
MPa |
| 薄膜 |
TensileStrength-TD |
屈服,51µm,吹塑薄膜 |
ASTMD882 |
11.7 |
MPa |
| 薄膜 |
抗张强度-MD |
Break,32µm,BlownFilm |
ASTMD882 |
24.1 |
MPa |
| 薄膜 |
抗张强度-MD |
断裂,51µm,吹塑薄膜 |
ASTMD882 |
20.0 |
MPa |
| 薄膜 |
TensileStrength-TD |
Break,32µm,BlownFilm |
ASTMD882 |
17.2 |
MPa |
| 薄膜 |
TensileStrength-TD |
断裂,51µm,吹塑薄膜 |
ASTMD882 |
17.2 |
MPa |
| 薄膜 |
伸长率-MD |
Break,32µm,BlownFilm |
ASTMD882 |
120 |
% |
| 薄膜 |
伸长率-MD |
断裂,51µm,吹塑薄膜 |
ASTMD882 |
230 |
% |
| 薄膜 |
TensileElongation-TD |
Break,32µm,BlownFilm |
ASTMD882 |
500 |
% |
| 薄膜 |
TensileElongation-TD |
断裂,51µm,吹塑薄膜 |
ASTMD882 |
540 |
% |
| 薄膜 |
落锤冲击 |
32µm,BlownFilm |
ASTMD1709 |
80 |
g |
| 薄膜 |
落锤冲击 |
50µm,吹塑薄膜 |
ASTMD1709 |
120 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD |
32µm,BlownFilm |
ASTMD1922 |
150 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD |
50µm,吹塑薄膜 |
ASTMD1922 |
450 |
g |
| 薄膜 |
ElmendorfTearStrength-TD |
32µm,BlownFilm |
ASTMD1922 |
150 |
g |
| 薄膜 |
ElmendorfTearStrength-TD |
50µm,吹塑薄膜 |
ASTMD1922 |
300 |
g |
| 光学性能 |
光泽度 |
45°,31.8µm,BlownFilm |
ASTMD2457 |
60 |
|
| 光学性能 |
光泽度 |
45°,50.8µm,BlownFilm |
ASTMD2457 |
67 |
|
| 光学性能 |
雾度 |
31.8µm,BlownFilm |
ASTMD1003 |
8.5 |
% |
| 光学性能 |
雾度 |
50.8µm,BlownFilm |
ASTMD1003 |
8.5 |
% |