| 规格级别 | 其它 其它 挤出 | 外观颜色 | |
| 该料用途 | 薄片 | ||
| 备注说明 | 低密度 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||
| 基本性能 | 密度 | ASTM D-1505 | 0.921 | g/m3 | ||||
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 2.7 | g/10min | ||||
| 机械性能 | 拉伸断裂强度 | Compression Molded | ASTM D-638 | 13 | MPa | |||
| 拉伸断裂伸长率 | Compression Molded | ASTM D-638 | 630 | % | ||||
| 薄膜厚度 | 38 | um | ||||||
| 拉伸断裂强度 | 38um,Blown Film | ASTM D-882 |
|
MPa | ||||
| 拉伸断裂伸长率 | 38um,Blown Film | ASTM D-882 |
|
% | ||||
| 落锤冲击 | 38um,Blown Film | ASTM D-1709 | 110 | g | ||||
| 埃尔曼多夫撕裂强度 | 38um | ASTM D-1922 | 190 | g | ||||
| 热性能 | 维卡软化点 | ASTM D-1525 | 93 | ℃ | ||||
| 光泽 | 60° | ASTM D-2457 | 12 | |||||
| 雾度 | ASTM D-1003 | 5 | ℃ | |||||