| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.918 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
2.3 |
g/10min |
| 机械性能 |
抗张强度(屈服) |
|
ASTMD638 |
8.80 |
MPa |
| 机械性能 |
伸长率(断裂) |
|
ASTMD638 |
710 |
% |
| 机械性能 |
弯曲模量-1%正割 |
|
ASTMD790 |
296 |
MPa |
| 机械性能 |
摩擦系数(吹塑薄膜) |
|
ASTMD1894 |
>0.60 |
|
| 薄膜 |
薄膜厚度-经测试 |
|
|
38 |
µm |
| 薄膜 |
SecantModulus-1%Secant,MD(38µm,BlownFilm) |
|
ASTMD882 |
150 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(38µm,BlownFilm) |
|
ASTMD882 |
175 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,38µm,BlownFilm) |
|
ASTMD882 |
10.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,38µm,BlownFilm) |
|
ASTMD882 |
9.00 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,38µm,BlownFilm) |
|
ASTMD882 |
18.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,38µm,BlownFilm) |
|
ASTMD882 |
16.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,38µm,BlownFilm) |
|
ASTMD882 |
350 |
% |
| 薄膜 |
TensileElongation-TD(Break,38µm,BlownFilm) |
|
ASTMD882 |
550 |
% |
| 薄膜 |
落锤冲击(38µm,吹塑薄膜) |
|
ASTMD1709A |
90 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(38µm,BlownFilm) |
|
ASTMD1922 |
230 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-TD(38µm,吹塑薄膜) |
|
ASTMD1922 |
150 |
g |
| 光学性能 |
Gloss(45°,38.0µm,BlownFilm) |
|
ASTMD2457 |
40 |
|
| 光学性能 |
雾度(38.0µm,吹塑薄膜) |
|
ASTMD1003 |
12 |
% |
| ADDITIONAL INFORMATION |
补充信息 |
|
TestMethod |
NominalValue |
Unit |
| ADDITIONAL INFORMATION |
MeltStrength |
|
|
0.500 |
g/3min |
| ADDITIONAL INFORMATION |
Puncture2(38.0µm) |
|
InternalMethod |
450 |
J/cm |