| 规格级别 | 其它 其它 挤出 | 外观颜色 | |
| 该料用途 | 收缩包装，包装，衬板，电影 | ||
| 备注说明 | 良好的熔体强度，食品接触的可接受，高清晰度，良好的耐冲击性能 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||
| 基本性能 | 密度 | ASTM D-1505 | 0.92 | g/cm3 | ||||
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.25 | g/10min | ||||
| 机械性能 | 邵氏硬度 | Shore D | ASTM D-2240 | 45 | ||||
| 拉伸屈服强度 | ASTM D-638 | 9.79 | MPa | |||||
| 拉伸断裂强度 | ASTM D-638 | 17.9 | MPa | |||||
| 拉伸屈服伸长率 | ASTM D-638 | 100 | % | |||||
| 拉伸断裂伸长率 | ASTM D-638 | 700 | % | |||||
| 薄膜厚度-Tested | 50.8 | um | ||||||
| 割线模量-1% Secant | 31.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸屈服强度 | 31.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸断裂伸长率 | 31.8um | ASTM D-882 |
|
% | ||||
| 落锤冲击 | 31.8um | ASTM D-1709 | 180 | g | ||||
| 电气性能 | 熔体温度 | 166-221 | ℃ | |||||
| 热性能 | 脆化温度 | ASTM D-746 | -75 | ℃ | ||||
| 维卡软化点 | ASTM D-1525 | 93 | ℃ | |||||