| 规格级别 | 其它 其它 挤出 | 外观颜色 | |
| 该料用途 | 工业应用，电影 | ||
| 备注说明 | 良好的加工，良好的降水，食品接触的可接受，高耐冲击性能，滑移，良好的强度 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||
| 基本性能 | 密度 | ASTM D-1505 | 0.919 | g/cm3 | ||||
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.7 | g/10min | ||||
| 机械性能 | 邵氏硬度 | Shore D | ASTM D-2240 | 46 | ||||
| 拉伸屈服强度 | ASTM D-638 | 10.7 | MPa | |||||
| 拉伸断裂强度 | ASTM D-638 | 11.4 | g/10min | |||||
| 拉伸屈服伸长率 | ASTM D-638 | 100 | % | |||||
| 拉伸断裂伸长率 | ASTM D-638 | 700 | % | |||||
| 薄膜厚度-Tested | 31.8 | um | ||||||
| 割线模量-1% Secant | 31.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸屈服强度 | 31.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸断裂伸长率 | 31.8um | ASTM D-882 |
|
% | ||||
| 落锤冲击 | 31.8um | ASTM D-1709 | 130 | g | ||||
| 埃尔曼多夫撕裂强度 | 31.8um | ASTM D-1922 |
|
g | ||||
| 加工性能 | 熔体温度 | 154-177 | ℃ | |||||
| 热性能 | 脆化温度 | ASTM D-746 | -75 | ℃ | ||||
| 维卡软化点 | ASTM D-1525 | 90 | ℃ | |||||