| 规格级别 | 其它 其它 挤出 | 外观颜色 | |
| 该料用途 | 瓶，玩具 | ||
| 备注说明 | 食品接触的可接受，良好的加工，较好的韧性，高清晰度 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||
| 基本性能 | 密度 | ASTM D-1505 | 0.918 | g/cm3 | ||||
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.25 | g/10min | ||||
| 机械性能 | 环境应力开裂 | 100% Igepal，F0 | ASTM D-1693 | 168 | hr | |||
| 邵氏硬度 | Shore D | ASTM D-2240 | 50 | |||||
| 拉抻断裂强度 | ASTM D-638 | 14.5 | MPa | |||||
| 拉伸断裂伸长率 | ASTM D-638 | 600 | % | |||||
| 弯曲模量 | ASTM D-790 | 234 | MPa | |||||
| 薄膜厚度-Tested | 50.8 | um | ||||||
| 割线模量-1% Secant | 50.8um | ASTM D-882 |
|
MPa | ||||
| 拉抻屈服强度 | 50.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸断裂伸长率 | 50.8um | ASTM D-882 |
|
% | ||||
| 落锤冲击 | 50.8um | ASTM D-1709 | 220 | g | ||||
| 埃尔曼多夫撕裂强度 | 50.8um | ASTM D-1922 |
|
g | ||||
| 热性能 | 热变形温度 | ASTM D-648 | 42 | ℃ | ||||
| 脆化温度 | ASTM D-746 | -76 | ℃ | |||||
| 维卡软化点 | ASTM D-1525 | 90 | % | |||||