| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.919 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.70 |
g/10min |
| 薄膜 |
SecantModulus-1%Secant,MD |
|
ASTMD882 |
200 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD |
|
ASTMD882 |
245 |
MPa |
| 薄膜 |
抗张强度-MD(屈服) |
|
ASTMD882 |
25.5 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield) |
|
ASTMD882 |
19.3 |
MPa |
| 薄膜 |
伸长率-MD(断裂) |
|
ASTMD882 |
150 |
% |
| 薄膜 |
TensileElongation-TD(Break) |
|
ASTMD882 |
500 |
% |
| 薄膜 |
落锤冲击(38µm) |
|
ASTMD1709 |
150 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(38µm) |
|
ASTMD1922 |
330 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(38µm) |
|
ASTMD1922 |
150 |
g |
| 光学性能 |
光泽度(45°,38.0µm) |
|
ASTMD2457 |
45 |
|
| 光学性能 |
雾度(38.0µm) |
|
ASTMD1003 |
15 |
% |