| 规格级别 | 可加工性，良好,光学性能 流延薄膜 | 外观颜色 | |
| 该料用途 | 包装,薄膜 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTMD1505 | 0.925 | g/cm³ | |
| 物理性能 | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 2.2 | g/10min | |
| 机械性能 | 摩擦系数(铸造薄膜) | ASTMD1894 | >1.0 | ||
| 薄膜 | 薄膜厚度-经测试 | 32 | µm | ||
| 薄膜 | 氧气传输速率(32µm,铸造薄膜) | ASTMD3985 | 6300 | cm³/m²/24hr | |
| 薄膜 | 水气透过率(32µm,铸造薄膜) | ASTMF1249 | 14 | g/m²/24hr | |
| 薄膜 | DartDropTest2(31.8µm) | ASTMD1709 | 30.9 | kN/m | |
| 薄膜 | ElmendorfTearStrength2 | MD:31.8µm | ASTMD1922 | 73.4 | kN/m |
| 薄膜 | ElmendorfTearStrength2 | TD:31.8µm | ASTMD1922 | 98.5 | kN/m |
| 薄膜 | 薄膜厚度-经测试 | 32 | µm | ||
| 薄膜 | 氧气传输速率(32µm,铸造薄膜) | ASTMD3985 | 6300 | cm³/m²/24hr | |
| 薄膜 | 水气透过率(32µm,铸造薄膜) | ASTMF1249 | 14 | g/m²/24hr | |
| 薄膜 | DartDropTest2(31.8µm) | ASTMD1709 | 30.9 | kN/m | |
| 薄膜 | ElmendorfTearStrength2 | MD:31.8µm | ASTMD1922 | 73.4 | kN/m |
| 薄膜 | ElmendorfTearStrength2 | TD:31.8µm | ASTMD1922 | 98.5 | kN/m |
| 热性能 | 维卡软化温度 | ASTMD1525 | 98.3 | °C | |
| 热性能 | 熔融峰值温度 | ASTMD3418 | 111 | °C | |
| 光学性能 | 光泽度(60°,31.8µm,铸造薄膜) | ASTMD2457 | 135 | ||
| 光学性能 | 雾度(31.8µm,铸造薄膜) | ASTMD1003 | 4.0 | % | |