LDPE | LD136
生产厂家：埃克森美孚
规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
|
| 该料用途 |
食品包装 |
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
最高熔体温度 |
|
ExxonMobil Method |
111 |
℃ |
| 密度 |
|
ExxonMobil Method |
0.921 |
g/cm3 |
| 熔体流动速率 |
|
ExxonMobil Method |
2.0 |
g/10min |
| 机械性能 |
1%割线模量 |
MD |
|
ASTM D-882 |
200 |
MPa |
| TD |
|
ASTM D-882 |
248 |
MPa |
| 断裂强度 |
MD |
|
ASTM D-882 |
25 |
MPa |
| TD |
|
ASTM D-882 |
19 |
MPa |
| Dart drop impact |
F50 |
ASTM D-1709 |
72 |
g/mil |
| 断裂伸长率 |
MD |
|
ASTM D-882 |
130 |
% |
| TD |
|
ASTM D-882 |
540 |
% |
| 屈服强度 |
MD |
|
ASTM D-882 |
8.5 |
% |
| TD |
|
ASTM D-882 |
5.8 |
% |
| Elmendorf Tear Strength |
MD |
|
ASTM D-1922 |
310 |
g/mil |
| TD |
|
ASTM D-1922 |
66 |
g/mil |
| 热性能 |
维卡软化点 |
|
ASTM D-1525 |
92 |
℃ |
| 其它性能 |
Haze |
|
ASTM D-1003 |
6.5 |
% |
| Gloss |
45℃ |
ASTM D-257 |
66 |
|
-
-